Product Specification: IOC Propel-1110 MG Injection Moulding Granule
Manufacturer: Indian Oil Corporation Ltd (IOCL) Brand: Propel Grade: 1110MG Plastic Family: Polypropylene (PP) Plastic Symbol: PP Homopolymer Manufacturing Technology: Latest Spheripol II Technology Physical Form: Granules Color: Natural
Key Features:
- High flow
- High Rigidity
- Excellent gloss
- Produced by Spheripol II Technology
Recommended Applications:
PP Homopolymer 1110MG is recommended for Injection Molded applications such as:
- Rigid Packaging
- Household articles
- Furniture
Typical Properties:
| Property | Value | Unit | Test Method |
|---|---|---|---|
| Resin Properties | |||
| Melt Flow Index (230°C & 2.16 Kg) | 11.0 | gm/10 min | ASTM D1238 |
| Density @ 23°C | 0.90 | gm/cm³ | ASTM D1505 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | 40 | MPa | ASTM D638 |
| Elongation @ Yield (50 mm/min) | 8 | % | ASTM D638 |
| Flexural Modulus (1.3 mm/min) | 1550 | MPa | ASTM D790 |
| Notched Izod Impact Strength @ 23°C | 21 | J/m | ASTM D256 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/m²) | 100 | °C | ASTM D648 |
| Vicat Softening Point (10 N) | 154 | °C | ASTM D1525 |
Note: Typical values not to be construed as specification limits. Values may change without any prior notice. Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Processing Information:
- Recommended Processing Temperature: 170 – 230 °C
Packaging Information:
- This material is packed and available in raffia bags with a net content of 25.0 Kg only.
- The raffia bags used conform to the minimum strength requirements of BIS.
- Customer shall take due care while handling the bag.
- Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause